Harris 0620F1 BRAZING ALLOY TUBE HARRIS O, 28 STICKS

Harris low cost alloy for many copper to copper applications where moderate fit-up can be maintained and brazing temperature is Not critical.

• Harris Low cost alloy suitable for most copper-to-copper or brass joints where good fit-up exists and assemblies are not subject to excessive vibration nor movement
• This alloy flows quickly at brazing temperature so requires close joint tolerance, less than 0005 in is a frequent choice for copper brazing
• A suitable choice for brazing brass, operators should take care to avoid over heating the brass and use Harris Stay-Silv white brazing flux in this application
• Not recommended for brazing steel or other ferrous base metals, the phosphorus content will form a low ductility intermetallic with the base metal
• Corrosion resistance is generally similar to copper base metal, but phosphorus containing alloys, including Harris , should not be used if the braze is exposed to sulfur or sulfur compounds in service

AWS A5.8 BCuP-2|ASME Section IIC SFA 5.8 BCuP-2|ISO 17672 CuP 181|PROP65: Cancer and Reproductive Harm - www.P65Warnings.ca.gov|RoHS Compliant